Application of New Al-Si Welding Filler with High Concentration of Copper and Magnesium: High-Temperature Strength and Anti-Corrosion Mechanism

Jun Ren Zhao, Fei Yi Hung, Chien Yu Pan

Research output: Contribution to journalArticlepeer-review

Abstract

Currently, the primary commercial aluminum alloy fillers used are 4043 and 5356. However, when welded with high-strength work pieces like 6061 and 7075 aluminum alloys, the strength of weld beads significantly lags behind that of the original welded material. Both 4043 and 5356 aluminum alloys cannot be strengthened through heat treatment. The strength difference between the weld bead and base material doubles after heat treatment. In this study, an Al-Si-Cu-Mg alloy (SCM) filler modified using a heat-treatable A319 aluminum alloy was employed to investigate the post-welding microstructural and mechanical properties of specimens under room- and high-temperature conditions and after prolonged exposure in a saltwater environment (3.5 wt.% NaCl). The aim was to demonstrate that commercial aluminum alloy fillers could be substituted with a high-silicon aluminum alloy boasting excellent solidification and mechanical properties. The results revealed that, after heat treatment of the weld bead, dendrites were not eliminated, but the tensile strength increased to 310 MPa, closely matching that of commercial 6061 aluminum alloy. The strength of the weld bead remained higher than 250 MPa in high-temperature (240 °C) and saltwater environments. These findings underscore the potential application of this material.

Original languageEnglish
Article number126
JournalMaterials
Volume17
Issue number1
DOIs
Publication statusPublished - 2024 Jan

All Science Journal Classification (ASJC) codes

  • General Materials Science
  • Condensed Matter Physics

Fingerprint

Dive into the research topics of 'Application of New Al-Si Welding Filler with High Concentration of Copper and Magnesium: High-Temperature Strength and Anti-Corrosion Mechanism'. Together they form a unique fingerprint.

Cite this