Characteristics of magnetic mesoparticles fabricated by electroless nickel deposition

Ming Kai Chang, Chun Han Chen, Bing-Hung Chen

Research output: Contribution to journalArticlepeer-review

4 Citations (Scopus)

Abstract

A low-cost wet chemical process, viz., the electroless nickel deposition, was successfully developed to produce magnetic nickel-tungsten-phosphorus (NiWP) mesoparticles with diameters ranging from 100 to 500 nm on silica templates of ca. 102 nm and gold templates of ca. 3 nm. An X-ray diffractometer (XRD), transmission electron microscope (TEM), scanning electron microscope (SEM) equipped with an energy-dispersive X-ray spectrometer (EDX), a superconducting quantum interference device (SQUID), and a vibrating sample magnetometer (VSM) were employed to characterize these particles. The averaged sizes of the NiWP particles could be conveniently regulated with the duration of the electroless plating process, in which exponential growth kinetics of the NiWP particles was observed. Both XRD and electrodiffraction (ED) patterns of these NiWP alloys indicate existence of diffraction peaks close to the (111), (200), (220), and (311) reflections of bulk face-centered cubic (fee) Ni. The zero-field-cooled (ZFC) and field-cooled (FC) measurements also indicate the irreversibility temperatures of magnetization of these particles are in between 300 and 380 K. Dependent on the plating baths, the Curie temperatures of the resulting NiWP particles are around 330 K and higher than 380 K. Hence, weak ferromagnetic behaviors were evidently observed on all of these NiWP particles. Their saturation magnetization and coercivity were found in the range from 6 to 28 emu/g of sample and from 26 to 50 Oe, respectively.

Original languageEnglish
Pages (from-to)3021-3029
Number of pages9
JournalIndustrial and Engineering Chemistry Research
Volume47
Issue number9
DOIs
Publication statusPublished - 2008 May 7

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Chemical Engineering(all)
  • Industrial and Manufacturing Engineering

Fingerprint Dive into the research topics of 'Characteristics of magnetic mesoparticles fabricated by electroless nickel deposition'. Together they form a unique fingerprint.

Cite this