Combustion synthesis of Si3N4 powder

Wei Chang Lee, Shyan-Lung Chung

Research output: Contribution to journalArticlepeer-review

50 Citations (Scopus)

Abstract

A combustion synthesis (SHS) process has been developed for the synthesis of Si3N4 powder under low nitrogen pressures. Si and NaN3 powders were used as the reactants, and NH4Cl powder was added as a catalytic agent. These powders were mixed and pressed into a cylindrical compact. The compact was wrapped up with an igniting agent (i.e., Ti + C), and the synthesis reaction was triggered by the combustion of the igniting agent. Addition of NH4Cl was found necessary for the combustion synthesis reaction under low nitrogen pressures (<1.2 MPa). The product as synthesized is mostly in the form of agglomerated fine particles (0.1-1 μm in diameter) and is composed mainly of α-phase and a minor amount of β-phase. Effects of various experimental parameters (N2 pressure, NaN3, NH4Cl, and Si3N4 contents) on the product conversion and the combustion temperature were investigated. A possible reaction mechanism was proposed that explains the effects of the experimental parameters on the synthesis reaction.

Original languageEnglish
Pages (from-to)805-811
Number of pages7
JournalJournal of Materials Research
Volume12
Issue number3
DOIs
Publication statusPublished - 1997 Jan 1

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Combustion synthesis of Si<sub>3</sub>N<sub>4</sub> powder'. Together they form a unique fingerprint.

Cite this