Crystal growth in dentinal tubules with bio-calcium carbonate-silica sourced from equisetum grass

Hao Hueng Chang, Chun Liang Yeh, Yin Lin Wang, Guan Wen Liu, Hong Ping Lin, Chun Pin Lin

Research output: Contribution to journalArticlepeer-review

4 Citations (Scopus)

Abstract

Background/Purpose: One effective way to deal with dentin hypersensitivity is to develop materials to seal the tubules. The porous bio-calcium carbonate-silica (BCCS) contained well-dispersed CaCO3 would form calcium phosphates to seal the dentinal tubules when mixed with an acidic solution. The acidic hydrothermal treatment and calcination to isolate the BCCS from the agricultural waste like equisetum grass was used, which would be more environmentally friendly than chemically synthesized mesoporous biomaterials. The aim of this study was to develop mesoporous materials from natural resources to occlude the dentinal tubules which could be more environmentally-friendly. Methods: Dentin disc samples were prepared and treated with different methods as follows: (1) BCCS mixed with H3PO4; (2) BCCS mixed with KH2PO4; (3) Seal & Protect® was used as a comparison group. Sealing efficacy was evaluated by measuring the depths and percentages of precipitate occlusion in dentinal tubules with SEM. Results: The N2 adsorption–desorption isotherm of the BCCS demonstrated a pore size of around 15.0 nm and a surface area of 61 m2g-1. From the results of occlusion percentage and depth, the BCCS treated with H3PO4 or KH2PO4 demonstrated promising sealing efficacy than the commercial product. Conclusion: This synthetic process used the agricultural waste equisetum grass to produce bio-calcium carbonate-silica would be environmentally friendly, which has great potential in treating exposed dentin related diseases.

Original languageEnglish
Pages (from-to)1835-1841
Number of pages7
JournalJournal of the Formosan Medical Association
Volume119
Issue number12
DOIs
Publication statusPublished - 2020 Dec

All Science Journal Classification (ASJC) codes

  • General Medicine

Fingerprint

Dive into the research topics of 'Crystal growth in dentinal tubules with bio-calcium carbonate-silica sourced from equisetum grass'. Together they form a unique fingerprint.

Cite this