T1 - Effect of carbonization temperature on the basic properties of woodceramics made from carbonized bamboo fiber and liquefied wood
AU - Hirose, Takashi
AU - Zhao, Binyuan
AU - Okabe, Toshihiro
AU - Yoshimura, Masahiro
PY - 2002/8/15
Y1 - 2002/8/15
N2 - In this paper, a new woodceramics from carbonized bamboo fiber and liquefied wood was developed and the effects of carbonization temperature on the dimension shrinkage, weight loss, density, compressive strength, and volume electrical resistivity of the woodceramics were investigated. The results show that, with the increase in the carbonization temperature, liquefied wood decompose and then combine with carbonized bamboo fiber, the dimension of sample almost keep constant, but its compressive strength was improved, and its electrical resistivity was reduced.
AB - In this paper, a new woodceramics from carbonized bamboo fiber and liquefied wood was developed and the effects of carbonization temperature on the dimension shrinkage, weight loss, density, compressive strength, and volume electrical resistivity of the woodceramics were investigated. The results show that, with the increase in the carbonization temperature, liquefied wood decompose and then combine with carbonized bamboo fiber, the dimension of sample almost keep constant, but its compressive strength was improved, and its electrical resistivity was reduced.
UR - http://www.scopus.com/inward/record.url?scp=0037103879&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0037103879&partnerID=8YFLogxK
U2 - 10.1023/A:1016558922110
DO - 10.1023/A:1016558922110
M3 - Article
AN - SCOPUS:0037103879
VL - 37
SP - 3453
EP - 3458
JO - Journal of Materials Science
JF - Journal of Materials Science
SN - 0022-2461
IS - 16
ER -