Enhancement of optical performance of near-UV nitride-based light emitting diodes with different aluminum composition barrier structure

C. K. Wang, Y. Z. Chiou, C. C. Hsiang, D. H. Lee, W. Y. Yan, W. S. Chen, C. M. Cheng, K. H. Chen, J. J. Tang, J. Lee

Research output: Contribution to journalArticlepeer-review

4 Citations (Scopus)

Abstract

In this work, the InGaN/AlGaN multiple-quantum-well (MQW) near-ultraviolet (UV) light-emitting diodes (LEDs) with different aluminum compositions in the barrier layers are investigated and fabricated. The aluminum compositions of LED I, II, and III are 0, 2.5, and 3.85%, respectively. The light output powers of LED I, II, and III at an injection current of 350 mA are 95.46, 135.48 mW, and 179.54 mW, respectively. The light output power measured from LED III was 88% larger than that of LED I. The peak external quantum efficiency was enhanced from 9.24 to 17.26%. This result was attributed to the improvement of carrier confinement in the active region by using AlGaN-based barrier layers. The hot-cold effect of LEDs as functions of junction temperature currently is a very important key issue for actual application to LEDs. As the temperature increased, the injected carriers became excited and easily escaped from the active layer. Thus, the light output power of the LED decreased as the temperature increased. Compared with LED I and LED II, the light output power of LED III with better carrier confinement was decreased more slowly with increasing temperature.

Original languageEnglish
Pages (from-to)1769-1772
Number of pages4
JournalPhysica Status Solidi (A) Applications and Materials Science
Volume211
Issue number8
DOIs
Publication statusPublished - 2014 Aug

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Electrical and Electronic Engineering
  • Materials Chemistry

Fingerprint

Dive into the research topics of 'Enhancement of optical performance of near-UV nitride-based light emitting diodes with different aluminum composition barrier structure'. Together they form a unique fingerprint.

Cite this