Failure mechanism of amorphous and crystalline Ta-N films in the Cu/Ta-N/Ta/SiO2 structure

Ching Chun Chang, J. S. Chen, Wu Shiung Hsu

Research output: Contribution to journalArticlepeer-review

27 Citations (Scopus)

Abstract

The diffusion barrier properties of as-deposited amorphous TaNx (x ≈ 0.5) and crystalline TaN between Cu and SiO2 have been investigated in Cu/Ta-N/Ta/SiO2 structures. The thermal reactions of Cu/TaNx/Ta/SiO2 and Cu/TaN/Ta/SiO2 after annealing in vacuum at 500 to 900°C were investigated by using sheet resistance measurements, glancing incident angle X-ray diffraction, scanning electron microscopy, energy-dispersive X-ray spectrometry, and Rutherford backscattering spectrometry. No significant reaction and change of sheet resistance were detected for both systems after annealing up to 800°C. As compared to TaN, TaNx exhibited better electrical properties and capability for preventing Cu diffusing through it However, the sheet resistance of both systems increased abruptly after annealing at 900°C, especially the TaNx system. The severe increase in sheet resistance corresponds to the deterioration of Cu surfaces. Broken holes were seen in the TaNx layer, which were the initial sites for the structural failure. The cause of failure in Cu/Ta-N/Ta/SiO2 stacks is discussed on the basis of the characteristics of Ta-N films upon heat-treatment.

Original languageEnglish
Pages (from-to)G746-G750
JournalJournal of the Electrochemical Society
Volume151
Issue number11
DOIs
Publication statusPublished - 2004 Jan 1

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Renewable Energy, Sustainability and the Environment
  • Surfaces, Coatings and Films
  • Electrochemistry
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Failure mechanism of amorphous and crystalline Ta-N films in the Cu/Ta-N/Ta/SiO<sub>2</sub> structure'. Together they form a unique fingerprint.

Cite this