Flux pinning at high magnetic field in melt-processed SmBa 2Cu3O7 with nanocrystalline Sm211/Nd422 additives

Ping Chi Hsieh, Shih Yun Chen, In Gann Chen, Maw Kuen Wu

Research output: Contribution to journalArticlepeer-review

3 Citations (Scopus)

Abstract

Nano-sized Sm2BaCuO5 ('Sm211') and Nd 4Ba2Cu2O10 ('Nd422') non-superconducting particles were prepared by a typical sol-gel process of mixing poly-acrylic acid (PAA) with metal ion solutions. Small amounts (1 to 1 × 10-2 wt%) of nano-sized Sm211 and Nd422 powders were mixed homogeneously with the precursors of Sm123 + 25 wt% Sm211 followed by the melt-texture processing in air. It is observed that superconducting properties of SmBCO with nano-Sm211 or nano-Nd422 additives were greatly enhanced and a clear secondary peak effect was observed. The scale rule analysis shows that the δTc pinning mechanism may be responsible for the Jc enhancement at high field. A systematic study of the relationship of J c(H, T) with different amounts of nm-Sm211 and/or Nd422 additions was performed to determine the optimum nano-particle doping contents and their pinning mechanisms respectively.

Original languageEnglish
Pages (from-to)S111-S118
JournalSuperconductor Science and Technology
Volume18
Issue number2
DOIs
Publication statusPublished - 2005 Feb 1

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Condensed Matter Physics
  • Metals and Alloys
  • Electrical and Electronic Engineering
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Flux pinning at high magnetic field in melt-processed SmBa <sub>2</sub>Cu<sub>3</sub>O<sub>7</sub> with nanocrystalline Sm211/Nd422 additives'. Together they form a unique fingerprint.

Cite this