Photoluminescence spectroscopy of Mg-doped GaN

J. K. Sheu, Y. K. Su, G. C. Chi, B. J. Pong, C. Y. Chen, C. N. Huang, W. C. Chen

Research output: Contribution to journalArticle

57 Citations (Scopus)

Abstract

We have grown Mg-doped GaN films by metalorganic chemical vapor deposition with various CP2Mg flow rates. After 750 °C postgrowth annealing, p-type GaN films with carrier concentrations and mobilities about 2 X 1017/cm3 and 10 cm2/V s, respectively, have been achieved. A dominant photoluminescence (PL) line around 2.9 eV was observed at room temperature. By studying the dependence of PL on excitation density at 20 K, the emission line around 2.95 eV can be attributed to a donor-to-acceptor pair transition rather than to a conduction band-to-impurity transition involving the Mg-related deep level. We suggest that the DAP transition line is caused by a Mg related deep level at about 510 meV above the valence band. It is much deeper than the acceptor level at 250 meV commonly produced by the Mg dopants.

Original languageEnglish
Pages (from-to)4590-4594
Number of pages5
JournalJournal of Applied Physics
Volume84
Issue number8
DOIs
Publication statusPublished - 1998 Oct 15

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Photoluminescence spectroscopy of Mg-doped GaN'. Together they form a unique fingerprint.

Cite this