Revelation of rutile phase by Raman scattering for enhanced photoelectrochemical performance of hydrothermally-grown anatase TiO 2 film

Hsun Wei Cho, Kuo Lun Liao, Jih Sheng Yang, Jih Jen Wu

Research output: Contribution to journalArticle

15 Citations (Scopus)

Abstract

Photoelectrochemical (PEC) performances of the anatase TiO 2 films hydrothermally grown on the seeded fluorine-doped tin oxide (FTO) substrates are examined in this work. Structural characterizations of the TiO 2 films were conducted using Raman scattering spectroscopy. Although there is no obvious rutile peak appearing, an asymmetrical peak centered at ∼399 cm −1 was observed in the Raman spectra of the TiO 2 films deposited either on the low-temperature-formed seed layers or with low concentrations of Ti precursor. The asymmetrical Raman shift can be deconvoluted into the B 1g mode of anatase and E g mode of rutile TiO 2 peaks centered at ∼399 cm −1 and ∼447 cm −1 , respectively. Therefore, a minute quantity of rutile phase was inspected in the anatase film using Raman scattering spectroscopy. With the same light harvesting ability, we found that the PEC performance of the anatase TiO 2 film was significantly enhanced as the minute quantity of rutile phase existing in the film. It is ascribed to the formation of the anatase/rutile heterojunction which is beneficial to the charge separation in the photoanode.

Original languageEnglish
Pages (from-to)125-132
Number of pages8
JournalApplied Surface Science
Volume440
DOIs
Publication statusPublished - 2018 May 15

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Condensed Matter Physics
  • Physics and Astronomy(all)
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films

Fingerprint Dive into the research topics of 'Revelation of rutile phase by Raman scattering for enhanced photoelectrochemical performance of hydrothermally-grown anatase TiO <sub>2</sub> film'. Together they form a unique fingerprint.

  • Cite this