Solubility and LPE growth of mixed REBa2Cu3O7-δ

Xiao-Ding Qi, G. K. Perkins, A. D. Caplin, J. L. MacManus-Driscoll

Research output: Contribution to journalConference article

5 Citations (Scopus)

Abstract

Liquid phase epitaxy (LPE) of REBa2Cu3O7-δ on lattice mismatched substrates requires high supersaturation. However, the solubility of RE's in the fluxes used for growing REBCO is not widely known. In order to precisely control the supersaturation during growth, the solubility of RE's in the Ba:Cu=2:5 solution were measured by inductively coupled plasma atomic emission spectrometry (ICP-AES). Mixing of the RE's in the solution has led to a large increase in the overall RE solubility and, therefore, increase of the growth rate and homogeneity of REBCO thick films grown by LPE. Films of mixed RE's with excellent in-plane c-texture and 100% density, have been grown on LaAlO3, NdGaO3, SrTiO3 YSZ, MgO and Ni/NiO substrates at a mean rate of 1 to 2 μm/min. Tc's of 91 K have been achieved and Jc's over 6×105 A/cm2 at 77 K.

Original languageEnglish
Pages (from-to)2897-2900
Number of pages4
JournalIEEE Transactions on Applied Superconductivity
Volume11
Issue number1 III
DOIs
Publication statusPublished - 2001 Mar 1
Event2000 Applied Superconductivity Conference - Virginia Beach, VA, United States
Duration: 2000 Sep 172000 Sep 22

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Solubility and LPE growth of mixed REBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub>'. Together they form a unique fingerprint.

Cite this