Study on characteristics of interfacial microstructure and electrical current mechanism in Sn-xZn/Al photovoltaic modules

Chia Wei Lin, Fei Yi Hung, Truan Sheng Lui, Di Jung Huang

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

The microstructural characteristics, bonding force and bulk resistance of photovoltaic (PV) aluminum modules made with three hypereutectic solder alloys, namely Sn-30Zn, Sn-50Zn and Sn-70Zn, were investigated. In the dipping step, the mechanism of bonding between pure aluminum ribbons and Sn-xZn solder alloys is via the Sn-xZn solder liquid phase penetrating into aluminum grain boundaries rather than forming intermetallic compound at the interface. After reflow for connecting PV aluminum ribbon and silicon substrate with Ag paste, an AgZn3 layer, whose thickness increases with increasing reflow time, formed at the solder/Ag interface. After bias aging, the Ag paste was consumed, the thickness of AgZn3 significantly increased and the bulk resistance increased. The bulk resistance of the modules with “Ag direction” (electrons move from Al to Ag) is slightly higher than that of modules with “Al direction” (electrons move from Ag to Al) due to more formation of AgZn3, which decreases the cross-section area of electrical current and increases the path of electrical current. Sn-50Zn/Al PV modules have good stability and high conductivity, and are competitive with PV modules made with copper ribbons.

Original languageEnglish
Pages (from-to)840-848
Number of pages9
JournalSolar Energy
Volume170
DOIs
Publication statusPublished - 2018 Aug

All Science Journal Classification (ASJC) codes

  • Renewable Energy, Sustainability and the Environment
  • Materials Science(all)

Fingerprint Dive into the research topics of 'Study on characteristics of interfacial microstructure and electrical current mechanism in Sn-xZn/Al photovoltaic modules'. Together they form a unique fingerprint.

  • Cite this