Taper PbZr 0.2Ti 0.8O 3 nanowire arrays: From controlled growth by pulsed laser deposition to piezopotential measurements

Yu Ze Chen, Te Hsiang Liu, Cheng Ying Chen, Chin Hung Liu, Szu Ying Chen, Wen Wei Wu, Zhong Lin Wang, Jr Hau He, Ying Hao Chu, Yu Lun Chueh

Research output: Contribution to journalArticle

22 Citations (Scopus)

Abstract

Single crystalline PbZr 0.2Ti 0.8 (PZT) nanowires arrays (NWAs) with taper morphology were epitaxially grown on SrTiO 3 (STO) substrate using pulse laser deposition. The taper morphology was attributed to the overcoating of PZT layer via a lateral growth of PZT clusters/adatoms during PZT NW growth. The growth window for PZT film or nanowire was systematically studied at varied temperatures and pressures. The proposed growth mechanism of the taper PZT NWAs was investigated from a layer by layer growth via Frank-Van Der Merwe growth, followed by a formation of three-dimensional islands via Stranski-Krastanow growth, and then axial growth on the lowest energy (001) plane with growth direction of [001] via vapor-solid growth mechanism. However, under certain conditions such as at higher or lower pressure (>400 or <200 mTorr) or substrate temperatures (>850 °C and <725 °C), formation of the PZT NWs is suppressed while the epitaxial PZT thin film via the layer-by-layer growth remains. The controllable growth directions of the PZT NWAs on (001), (110), and (111) STO substrates were demonstrated. The piezopotential of the taper PZT NWAs using a conducting atomic force microscope with the average voltage output of ∼18 mV was measured. The theoretical piezopotential of a PZT NW was calculated to compare with the measured outputs, providing a comprehensively experimental and theoretical understanding of the piezoelectricity for the PZT NW.

Original languageEnglish
Pages (from-to)2826-2832
Number of pages7
JournalACS Nano
Volume6
Issue number3
DOIs
Publication statusPublished - 2012 Mar 27

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Engineering(all)
  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Taper PbZr <sub>0.2</sub>Ti <sub>0.8</sub>O <sub>3</sub> nanowire arrays: From controlled growth by pulsed laser deposition to piezopotential measurements'. Together they form a unique fingerprint.

  • Cite this

    Chen, Y. Z., Liu, T. H., Chen, C. Y., Liu, C. H., Chen, S. Y., Wu, W. W., Wang, Z. L., He, J. H., Chu, Y. H., & Chueh, Y. L. (2012). Taper PbZr 0.2Ti 0.8O 3 nanowire arrays: From controlled growth by pulsed laser deposition to piezopotential measurements. ACS Nano, 6(3), 2826-2832. https://doi.org/10.1021/nn300370m