Texture and magnetic properties of electrodeposited FePd films

Hung Pin Lin, Jui Chao Kuo

Research output: Contribution to journalArticlepeer-review

14 Citations (Scopus)


FePd films were deposited on brass substrates through electrodeposition using an alkaline electrolyte, which were annealed at 500, 600, and 700 °C for 1 h to form the ordered γ1-FePd fct phase. After annealing, the γ1-FePd fct phase is observed at 500, 600 and 700°C. FePd films show the normal direction close to <101>, <111> and <421> directions after annealing 500, 600 and 700 °C, respectively. After annealing 500, 600 and 700°C the average area grain size is 0.28 μm, 0.37 μm and 1.22 μm, respectively. The maximum coercivity H c of 309 Oe observed at 500 °C can be explained with both effects of the <001> easy axis and the small grain size.

Original languageEnglish
Pages (from-to)3537-3539
Number of pages3
JournalMaterials Letters
Issue number23-24
Publication statusPublished - 2011 Dec

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering


Dive into the research topics of 'Texture and magnetic properties of electrodeposited FePd films'. Together they form a unique fingerprint.

Cite this