The thermomechanical behavior for aluminum alloy under uniaxial tensile loading

H. T. Lee, G. H. Shaue

Research output: Contribution to journalArticle

30 Citations (Scopus)

Abstract

This paper studies temperature variation phenomenon induced by the thermomechanical effect in aluminum alloys 2024-T3 and 7075-T6 under uniaxial tensile loading. Experimental results show that cooling occurs under elastic deformation. When load yielding is attained the temperature approaches its minimum. Beyond the temperature minimum the slope of the temperature curve inverts and becomes positive as heating occurs under plastic deformation. The point of temperature curve inversion coincides with the point at which the sample's elastic behavior yields to stress and becomes plastic. At strain rates of 2×10-2 s-1-2×10-4 s-1, the amount of temperature drop was found to be reasonably close to the theoretical values, as determined by the standard thermoelastic model. Likewise, within this strain range, the relative difference between the stress value at lowest temperature and the stress value at the yielding point was minimum. Experiments demonstrate that the temperature method of defining yield strength is a valid technique and, moreover, for the aluminum alloys tested, superior to the tensile method, at least within the strain rate range of 2×10-2 s-1-2×10-4 s-1. The curve of experimental estimated thermoelastic factor, Km, showed two different regions when plotted in relation to strain rate. The two regions had inverse slopes and dramatically different curve characteristics. The regions met at a strain rate of about 10-3 s-1, which was also the point of closest approach to the theoretical values.

Original languageEnglish
Pages (from-to)154-164
Number of pages11
JournalMaterials Science and Engineering A
Volume268
Issue number1-2
DOIs
Publication statusPublished - 1999 Aug 15

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'The thermomechanical behavior for aluminum alloy under uniaxial tensile loading'. Together they form a unique fingerprint.

  • Cite this