Thermal and X-ray analysis of polymorphic crystals, melting, and crystalline transformation in poly(butylene adipate)

Eamor Woo, Ming Chien Wu

Research output: Contribution to journalArticle

61 Citations (Scopus)

Abstract

Polymorphic crystals and complex multiple melting behavior in an aliphatic biodegradable polyester, poly(butylene adipate) (PBA), were thoroughly examined by wide-angle X-ray diffraction (WAXD) and differential scanning calorimetry (DSC). Further clarification on mechanisms of multiple melting peaks related to polymorphic crystal forms in PBA was attempted. More stable α-form crystal is normally favored for crystallization from melt at higher temperatures (31-35 °C), or upon slow cooling from the melt; while the β-form is the favored species for crystallization at low temperatures (25-28 °C). We further proved that PBA crystallization could also result in all α-form even at low temperatures (25-28 °C) if it crystallized with the presence of prior α-form nuclei. PBA packed with both crystal forms could display as many as four melting peaks (P1-P4, in ascending temperature order). However, PBA initially containing only the α-crystal exhibited dual melting peaks of P1 and P3, which are attributed to dual lamellar distributions of the α-crystal. By contrast, PBA initially containing only the β-crystal could also exhibit dual melting peaks (P2 and P4) upon scanning. While P2 is clearly associated with melting of the initial β-crystal, the fourth melting peak (P4), appearing rather broad, was determined to be associated with superimposed thermal events of crystal transformation from β- to α-crystal and final re-melting of the new re-organized α-crystal. Crystal transformation from one to the other or vice versa, lamellae thickening, annealing at molten state, and influence on crystal polymorphism in PBA were analyzed. Relationships and mechanisms of dual peaks for isolate α- or β-crystals in PBA are discussed.

Original languageEnglish
Pages (from-to)1662-1672
Number of pages11
JournalJournal of Polymer Science, Part B: Polymer Physics
Volume43
Issue number13
DOIs
Publication statusPublished - 2005 Jul 1

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Physical and Theoretical Chemistry
  • Polymers and Plastics
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Thermal and X-ray analysis of polymorphic crystals, melting, and crystalline transformation in poly(butylene adipate)'. Together they form a unique fingerprint.

  • Cite this