A free-standing carbon nanofiber interlayer for high-performance lithium-sulfur batteries

Richa Singhal, Sheng Heng Chung, Arumugam Manthiram, Vibha Kalra

研究成果: Article同行評審

253 引文 斯高帕斯(Scopus)

摘要

Free-standing porous carbon nanofibers with tunable surface area and pore structure have been investigated as an interlayer between the sulfur cathode and the separator to inhibit the shuttling of the intermediate polysulfides in lithium-sulfur (Li-S) batteries. Specifically, the effects of thickness, surface area, and pore size distribution of carbon nanofiber (CNF) interlayers on the performance of Li-S batteries have been studied. The carbon nanofiber interlayer not only reduces the electrochemical resistance but also localizes the migrating polysulfides and traps them, thereby improving the discharge capacity as well as cyclability. It was found that the optimum thickness of the interlayer is a critical factor to achieve good cell performance, in addition to the surface area and pore structure. A high initial discharge capacity of 1549 mA h g-1 at C/5 rate, which is 92% of the theoretical capacity of sulfur, with 98% average coulombic efficiency and 83% capacity retention after 100 cycles was obtained with a meso-microporous carbon nanofiber interlayer. This journal is

原文English
頁(從 - 到)4530-4538
頁數9
期刊Journal of Materials Chemistry A
3
發行號8
DOIs
出版狀態Published - 2015 一月 1

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Renewable Energy, Sustainability and the Environment
  • Materials Science(all)

指紋 深入研究「A free-standing carbon nanofiber interlayer for high-performance lithium-sulfur batteries」主題。共同形成了獨特的指紋。

引用此