A low-loss, low temperature sintering dielectric using Ba1-xSrxMg2(VO4)2 ceramics and its applications at microwave frequencies

Cheng Liang Huang, Tsung Min Chu, Meng Hung Tsai

研究成果: Article同行評審

摘要

Polycrystalline Ba1-xSrxMg2(VO4)2 compounds were investigated as a promising microwave dielectric for low-temperature co-fired ceramics (LTCC) applications. The single tetragonal phase was detected for the BaMg2(VO4)2 compound, and a phase transition from BaMg2(VO4)2 to SrMg2(VO4)2 was observed with an increase in the Sr substitution. The Raman spectrum was recorded to clarify the vibration and rotation modes of the specimen. The τf values was improved dramatically from –42.8 to –4.5 ppm/°C with a minute Sr substitution (x = 0.15) in place of Ba. Combined excellent microwave dielectric properties (εr ~ 13.1, Q × f ~ 71,000 GHz and τf ~ –4.5 ppm/°C) can be obtained for specimens using Ba0.85Sr0.15Mg2(VO4)2 sintered at 950 °C for 4 h. In addition, an U-type band-pass filter with two transmission zeroes was designed and fabricated on the ceramic substrates. Not only the circuit size was reduced, an excellent filter performance was also obtained. Thus, these compounds constitute very promising materials for LTCC applications.

原文English
文章編號115114
期刊Materials Science and Engineering B: Solid-State Materials for Advanced Technology
268
DOIs
出版狀態Published - 2021 六月

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

指紋 深入研究「A low-loss, low temperature sintering dielectric using Ba<sub>1-</sub><sub>x</sub>Sr<sub>x</sub>Mg<sub>2</sub>(VO<sub>4</sub>)<sub>2</sub> ceramics and its applications at microwave frequencies」主題。共同形成了獨特的指紋。

引用此