T1 - A new phase of cadmium titanate by hydrothermal method
AU - Wang, Hao
AU - Zhang, Xiao Xue
AU - Huang, An Ping
AU - Xu, Hai Yan
AU - Zhu, Man Kang
AU - Wang, Bo
AU - Yan, Hui
AU - Yoshimura, Masahiro
PY - 2002/12/1
Y1 - 2002/12/1
N2 - A new phase of cadmium titanate was prepared by hydrothermal method under low temperature of 120°C. The electron diffraction investigation showed that the structure of the new phase is hexagonal with lattice parameters a = b = 5.2099 Å and c = 4.6811 Å, which have been calibrated by its X-ray diffraction pattern. The X-ray photoelectron spectroscopy results suggested that the new phase can be described as CdTiO3. Furthermore, it was observed that the post-annealing at 700°C and 1050°C led to the transition of the new phase to the known ilmenite and then perovskite phase, respectively.
AB - A new phase of cadmium titanate was prepared by hydrothermal method under low temperature of 120°C. The electron diffraction investigation showed that the structure of the new phase is hexagonal with lattice parameters a = b = 5.2099 Å and c = 4.6811 Å, which have been calibrated by its X-ray diffraction pattern. The X-ray photoelectron spectroscopy results suggested that the new phase can be described as CdTiO3. Furthermore, it was observed that the post-annealing at 700°C and 1050°C led to the transition of the new phase to the known ilmenite and then perovskite phase, respectively.
UR - http://www.scopus.com/inward/record.url?scp=0036888387&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0036888387&partnerID=8YFLogxK
U2 - 10.1016/S0022-0248(02)01761-X
DO - 10.1016/S0022-0248(02)01761-X
M3 - Article
AN - SCOPUS:0036888387
VL - 246
SP - 150
EP - 154
JO - Journal of Crystal Growth
JF - Journal of Crystal Growth
SN - 0022-0248
IS - 1-2
ER -