A novel Al and Y codoped ZnO/n-Si heterojunction solar cells fabricated by pulsed laser deposition

Feng Hao Hsu, Na Fu Wang, Yu Zen Tsai, Mau-phon Houng

研究成果: Article

21 引文 斯高帕斯(Scopus)

摘要

Al and Y codoped ZnO (AZOY) transparent conducting oxide (TCO) thin films were first deposited on n-Si substrates by pulsed laser deposition (PLD) to form AZOY/n-Si heterojunction solar cells. However, the properties of the AZOY emitter layers are critical to the performance of AZOY/n-Si heterojunction solar cells. To estimate the properties of AZOY thin films, films deposited on glass substrates with various substrate temperatures (T s) were analyzed. Based on the experimental results, optimal electrical properties (resistivity of 2.8±0.14×10 -4Ωcm, carrier mobility of 27.5±0.55cm 2/Vs, and carrier concentration of 8.0±0.24×10 20cm -3) of the AZOY thin films can be achieved at a T s of 400°C, and a high optical transmittance of AZOY is estimated to be >80% (with glass substrate) in the visible region under the same T s. For the AZOY/n-Si heterojunction solar cells, the AZOY thin films acted not only as an emitter layer material, but also as an anti-reflected coating thin film. Thus, a notably high short-circuit current density (J sc) of 31.51±0.186mA/cm 2 was achieved for the AZOY/n-Si heterojunction solar cells. Under an AM1.5 illumination condition, the conversion efficiency of the cells is estimated at only approximately 4% (a very low open-circuit voltage (V oc) of 0.24±0.001V and a fill factor (FF) of 0.51±0.011) without any optimization of the device structure.

原文English
頁(從 - 到)3146-3152
頁數7
期刊Solar Energy
86
發行號11
DOIs
出版狀態Published - 2012 十一月 1

    指紋

All Science Journal Classification (ASJC) codes

  • Renewable Energy, Sustainability and the Environment
  • Materials Science(all)

引用此