TY - JOUR
T1 - A Rapid, Efficient Method for Anodic Aluminum Oxide Membrane Room-Temperature Multi-Detachment from Commercial 1050 Aluminum Alloy
AU - Ku, Chin An
AU - Hung, Chia Wei
AU - Chung, Chen Kuei
N1 - Publisher Copyright:
© 2024 by the authors.
PY - 2024/7
Y1 - 2024/7
N2 - For commercial processes, through-hole AAO membranes are fabricated from high-purity aluminum by chemical etching. However, this method has the disadvantages of using heavy-metal solutions, creating large amounts of material waste, and leading to an irregular pore structure. Through-hole porous alumina membrane fabrication has been widely investigated due to applications in filters, nanomaterial synthesis, and surface-enhanced Raman scattering. There are several means to obtain freestanding through-hole AAO membranes, but a fast, low-cost, and repetitive process to create complete, high-quality membranes has not yet been established. Here, we propose a rapid and efficient method for the multi-detachment of an AAO membrane at room temperature by integrating the one-time potentiostatic (OTP) method and two-step electrochemical polishing. Economical commercial AA1050 was used instead of traditional high-cost high-purity aluminum for AAO membrane fabrication at 25 °C. The OTP method, which is a single-step process, was applied to achieve a high-quality membrane with unimodal pore distribution and diameters between 35 and 40 nm, maintaining a high consistency over five repetitions. To repeatedly detach the AAO membrane, two-step electrochemical polishing was developed to minimize damage on the AA1050 substrate caused by membrane separation. The mechanism for creating AAO membranes using the OTP method can be divided into three major components, including the Joule heating effect, the dissolution of the barrier layer, and stress effects. The stress is attributed to two factors: bubble formation and the difference in the coefficient of thermal expansion between the AAO membrane and the Al substrate. This highly efficient AAO membrane detachment method will facilitate the rapid production and applications of AAO films.
AB - For commercial processes, through-hole AAO membranes are fabricated from high-purity aluminum by chemical etching. However, this method has the disadvantages of using heavy-metal solutions, creating large amounts of material waste, and leading to an irregular pore structure. Through-hole porous alumina membrane fabrication has been widely investigated due to applications in filters, nanomaterial synthesis, and surface-enhanced Raman scattering. There are several means to obtain freestanding through-hole AAO membranes, but a fast, low-cost, and repetitive process to create complete, high-quality membranes has not yet been established. Here, we propose a rapid and efficient method for the multi-detachment of an AAO membrane at room temperature by integrating the one-time potentiostatic (OTP) method and two-step electrochemical polishing. Economical commercial AA1050 was used instead of traditional high-cost high-purity aluminum for AAO membrane fabrication at 25 °C. The OTP method, which is a single-step process, was applied to achieve a high-quality membrane with unimodal pore distribution and diameters between 35 and 40 nm, maintaining a high consistency over five repetitions. To repeatedly detach the AAO membrane, two-step electrochemical polishing was developed to minimize damage on the AA1050 substrate caused by membrane separation. The mechanism for creating AAO membranes using the OTP method can be divided into three major components, including the Joule heating effect, the dissolution of the barrier layer, and stress effects. The stress is attributed to two factors: bubble formation and the difference in the coefficient of thermal expansion between the AAO membrane and the Al substrate. This highly efficient AAO membrane detachment method will facilitate the rapid production and applications of AAO films.
UR - http://www.scopus.com/inward/record.url?scp=85199863032&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=85199863032&partnerID=8YFLogxK
U2 - 10.3390/nano14141216
DO - 10.3390/nano14141216
M3 - Article
AN - SCOPUS:85199863032
SN - 2079-4991
VL - 14
JO - Nanomaterials
JF - Nanomaterials
IS - 14
M1 - 1216
ER -