Advances in selective wet etching for nanoscale NiPt salicide fabrication

Ming Mao Chu, Jung Hua Chou

研究成果: Article同行評審

2 引文 斯高帕斯(Scopus)

摘要

Currently, the two-step rapid thermal process (RTP) which includes a lower temperature RTP 1 and a larger amount of platinum (Pt) additive is the trend to form thinner nickel monosilicide (NiSi) for the NiPt silicide scaling together with complementary metal oxide semiconductor (CMOS) technology toward the 22nm node. In this work, we re-investigate the piranha chemistry and match the Pt oxidation/dissolution behavior to develop a piranha chemistry base wet etching process. The result shows that higher temperature preheated sulfuric acid Piranha will boost the reaction rate drastically. Also, the two-time Pt additive will take three-time process time to clear the Pt residue. Compare to the traditional chloric acid base process, the new Piranha process has achieved the goal of effective Pt removal, lower material loss and no damage to nickel-rich silicide (Ni2Si/Ni3Si2). It results in a lower and more uniform silicide sheet resistance (RS) on both n/pMOS.

原文English
頁(從 - 到)06GG161-06GG165
期刊Japanese journal of applied physics
49
發行號6 PART 2
DOIs
出版狀態Published - 2010 六月 1

All Science Journal Classification (ASJC) codes

  • Engineering(all)
  • Physics and Astronomy(all)

指紋 深入研究「Advances in selective wet etching for nanoscale NiPt salicide fabrication」主題。共同形成了獨特的指紋。

引用此