Ag precipitation at the free interface of multilayer NiCuZn ferrites/LTCC components

Hsing I. Hsiang, Bing Jyun Lyu, Li Then Mei, Chi Shiung Hsi

研究成果: Article同行評審

7 引文 斯高帕斯(Scopus)

摘要

The diffusion and precipitation of silver and copper in low-dielectric-constant low temperature cofired ceramics (LTCC) for multilayer NiCuZn ferrites/LTCC components are investigated in this study. Ag precipitation is formed at the free interface between NiCuZn ferrites and LTCC for multilayer NiCuZn ferrites/LTCC components after cofiring. During the heating stage Cu+ will segregate into the grain boundary from the NiCuZn ferrites due to the low oxygen partial pressure inside the sample and then dissolve into LTCC near the interface between NiCuZn ferrites and LTCC. Cu+ in glass would diffuse from the interior toward the surface and become oxidized into Cu2+ or precipitated as the CuO phase at the surface. To maintain charge neutrality this process requires an outward diffusion of Cu+ and Ag+ from the interior toward the free surface. The reduction of Ag+ into Ag on the free surface is accelerated by Cu+ oxidation.

原文English
頁(從 - 到)1191-1195
頁數5
期刊Journal of the European Ceramic Society
36
發行號5
DOIs
出版狀態Published - 2016 四月 1

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Materials Chemistry

指紋 深入研究「Ag precipitation at the free interface of multilayer NiCuZn ferrites/LTCC components」主題。共同形成了獨特的指紋。

引用此