Al2O3-YAG-ZrO2 ternary ceramics from melts

J. M. Calderon-Moreno, M. Yoshimura

研究成果: Conference article同行評審

2 引文 斯高帕斯(Scopus)

摘要

High temperature ceramic composites were obtained by rapid solidification from melts in the ternary oxide system Al2O3-Y2O3-ZrO2. The composition and stoichiometry of crystallized phases were determined by means of XRD analysis. Microstructural features were studied by means of SEM and optical microscopy. Quasi-binary eutectic composites were solidified near the alumina-zirconia binary line. Ternary composites containing alumina, zirconia-based solid solution and yttrium aluminum garnet (YAG) showed ordered structures in their SEM micrographs. The formation of quasi-ternary eutectic microstructures was observed.

原文English
頁(從 - 到)993-996
頁數4
期刊Key Engineering Materials
206-213
發行號II
出版狀態Published - 2001 1月 1
事件7th Conference and Exhibition of the European Ceramic Society - Brugge, Belgium
持續時間: 2001 9月 92001 9月 13

All Science Journal Classification (ASJC) codes

  • 材料科學(全部)
  • 材料力學
  • 機械工業

指紋

深入研究「Al2O3-YAG-ZrO2 ternary ceramics from melts」主題。共同形成了獨特的指紋。

引用此