An investigation into the crystallization and electric flame-off characteristics of 20 μm copper wires

Fei Yi Hung, Truan Sheng Lui, Li Hui Chen, Hao Wen Hsueh

研究成果: Article同行評審

16 引文 斯高帕斯(Scopus)

摘要

Copper wires are used in electronic packaging, however the workability and reliability still need to be improved. This work investigates the microstructural characteristics and mechanical properties of annealed wires and un-annealed wires. In addition, the interface bonding characteristics of Al pads are also studied. Experimental results indicate that at the two annealing conditions of 610 °C/0.02 s and 510 °C/0.4 s, 20 μm copper wires possessed a fully annealed structure. Compared with the un-annealed wire, the annealed tensile strength and the annealed hardness decreased, and the annealed elongation increased. Through thermal crystallization, the matrix structure transformed from long, thin grains to equiaxed grains and a few annealed twins. The microstructure of the free air ball (FAB) after an EFO process consisted of column-like grains, and grew from the heat-affected zone (HAZ) to the Cu ball. As for bonding testing, the pull strength of the bonded samples increased with increasing the Al film thickness (from 76 nm to 800 nm).

原文English
頁(從 - 到)21-24
頁數4
期刊Microelectronics Reliability
51
發行號1
DOIs
出版狀態Published - 2011 一月

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Atomic and Molecular Physics, and Optics
  • Safety, Risk, Reliability and Quality
  • Condensed Matter Physics
  • Surfaces, Coatings and Films
  • Electrical and Electronic Engineering

指紋 深入研究「An investigation into the crystallization and electric flame-off characteristics of 20 μm copper wires」主題。共同形成了獨特的指紋。

引用此