Analysis of Fermi level pinning and surface state distribution in InAlAs heterostructures

Wei-Yang Chou, Shih-hui Chang, W. C. Hwang, J. S. Hwang

研究成果: Article同行評審

12 引文 斯高帕斯(Scopus)

摘要

The band gaps, built-in electric field, and surface Fermi level of a series In 1 - x Al x As surface-intrinsic-n + (SW + ) structures have been studied by photoreflectance at room temperature. The samples were grown by molecular beam epitaxy with an undoped layer thickness of 1000 Å. Our study indicates that, in contrast to GaAs and AlGaAs, the surface Fermi level is not pinned at midgap over aluminum concentration of 0.42-0.57. The pinning position is composition dependent. The undoped layer was subsequently etched to 800, 600, 400, and 200 Å. Different chemical solutions were used in the etching process and the built-in electric field is found independent of the etching process. Although the surface Fermi level, in general, varies with the undoped layer thicknesses, there exists, for each Al concentration, a certain range of thicknesses within which the surface Fermi level is weakly pinned. From the dependence of electric field and surface Fermi level on the undoped layer thickness, we conclude that the surface states distribute over two separate regions within the energy band gap and the densities of surface states are as low as 1.36±0.05 ×10 11 cm -2 eV -1 for the distribution near the conduction band and 4.38±0.05×10 11 cm -2 eV -1 for the distribution near valence band.

原文English
頁(從 - 到)3690-3695
頁數6
期刊Journal of Applied Physics
83
發行號7
DOIs
出版狀態Published - 1998 一月 1

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

指紋 深入研究「Analysis of Fermi level pinning and surface state distribution in InAlAs heterostructures」主題。共同形成了獨特的指紋。

引用此