Anisotropic pinning-effect of inclusions in Mg-based low-carbon steel

Chi Kang Lin, Hsuan Hao Lai, Yen Hao Frank Su, Guan Ru Lin, Weng Sing Hwang, Jui Chao Kuo

研究成果: Article同行評審

摘要

In this study, the effect of austenite grain size on acicular ferrite (AF) nucleation in low-carbon steel containing 13 ppm Mg is determined. The average austenite grain size was calculated using OM Leica software. Results show that the predicted and experimental values of austenite grain size are extremely close, with a deviation of less than 20 μm. AF formation is difficult to induce by either excessively small and large austenite grain sizes; that is, an optimal austenite grain size is required to promote AF nucleation probability. The austenite grain size of 164 μm revealed the highest capacity to induce AF formation. The effects of the maximum distance of carbon diffusion and austenite grain size on the microstructure of Mg-containing low carbon steel are also discussed. Next, the pinning ability of different inclusion types in low-carbon steel containing 22 Mg is determined. The in situ observation shows that not every inclusion could inhibit austenite grain migration; the inclusion type influences pinning ability. The grain mobility of each inclusion was calculated using in situ micrographs of confocal scanning laser microscopy (CSLM) for micro-analysis. Results show that the austenite grain boundary can strongly be pinned by Mg-based inclusions. MnS inclusions are the least effective in pinning austenite grain boundary migration.

原文English
文章編號2241
期刊Materials
11
發行號11
DOIs
出版狀態Published - 2018 十一月 11

All Science Journal Classification (ASJC) codes

  • Materials Science(all)

指紋 深入研究「Anisotropic pinning-effect of inclusions in Mg-based low-carbon steel」主題。共同形成了獨特的指紋。

引用此