Antibacterial efficacy of chitosan- and poly(hexamethylene biguanide)-immobilized nanofiber membrane

I. Son Ng, Chien Wei Ooi, Bing Lan Liu, Chun To Peng, Chen Yaw Chiu, Yu Kaung Chang

研究成果: Article

3 引文 斯高帕斯(Scopus)

摘要

In this study, polyacrylonitrile (PAN) nanofiber membrane was prepared by an electrospinning technique. After alkaline hydrolysis, the ion-exchange nanofiber membrane (P-COOH) was grafted with chitosan molecules to form a chitosan-modified nanofiber membrane (P-COOH-CS). Poly(hexamethylene biguanide) (PHMB) was then covalently immobilized on P-COOH and P-COOH-CS to form P-COOH-PHMB and P-COOH-CS-PHMB, respectively. The nanofiber membranes were subjected to various surface analyses as well as to the evaluations of antibacterial activity against Escherichia coli. The optimal modification conditions for P-COOH-CS-PHMB were attained by water-soluble chitosan at 50 kDa of molecular weight, coupling pH at 7, and 0.05% (w/w) of PHMB. Within 10 min of treatment, the antibacterial rate was close to 100%. Under the similar conditions of antibacterial treatment, the P-COOH-CS-PHMB exhibited a better antibacterial efficacy than the P-COOH-PHMB. When the number of bacterial cells was increased by 2000 folds, both types of nanofiber membranes still maintained the antibacterial rate close to 100%. After five cycles of repeated antibacterial treatment, the antibacterial efficacy of P-COOH-PHMB was 96%, which was higher than that of P-COOH-CS-PHMB (83%). The experimental results revealed that the PHMB-modified nanofiber membranes can be suitably applied in water treatment such as water disinfection and biofouling control.

原文English
頁(從 - 到)844-854
頁數11
期刊International Journal of Biological Macromolecules
154
DOIs
出版狀態Published - 2020 七月 1

All Science Journal Classification (ASJC) codes

  • Structural Biology
  • Biochemistry
  • Molecular Biology
  • Economics and Econometrics
  • Energy(all)

指紋 深入研究「Antibacterial efficacy of chitosan- and poly(hexamethylene biguanide)-immobilized nanofiber membrane」主題。共同形成了獨特的指紋。

  • 引用此