Bipolar material with spiro-fluorenyl terminals: Synthesis, characterization and application for enhancement of electrophosphorescence

Chia Shing Wu, Juin Wei Wu, Yun Chen

研究成果: Article同行評審

19 引文 斯高帕斯(Scopus)

摘要

We have designed a novel bipolar material (FTzCz) consisting of spiro-fluorenyl terminals and a bipolar core to enhance emission efficiency of phosphorescent light-emitting diodes based on a conventional poly(9-vinylcarbazole) host and Ir(ppy) 3 dopant. The core is composed of directly linked hole-transporting carbazolyl and electron-affinitive aromatic 1,2,4-triazolyl groups. The bipolar FTzCz was synthesized by the Suzuki coupling reaction and was well characterized. It exhibited not only good thermal stability due to its rigid and non-planar chemical structure, but also facilitated hole- and electron-affinities simultaneously. Blending the bipolar FTzCz with PVK significantly enhanced the performance of electrophosphorescent devices [ITOPEDOT:PSS(PVK + FTzCz):Ir(ppy) 3 (4 wt%)BCP (10 nm)Ca (50 nm)Al (100 nm)]. The maximum luminance and maximum luminance efficiency were enhanced from 3550 cd m -2 and 5.6 cd A -1 (neat PVK-based device) to 4510 cd m -2 and 9.9 cd A -1 (blend device with PVK:FTzCz = 8:2), respectively. Our results demonstrate the efficacy of the bipolar FTzCz in enhancing performance of electrophosphorescent devices.

原文English
頁(從 - 到)23877-23884
頁數8
期刊Journal of Materials Chemistry
22
發行號45
DOIs
出版狀態Published - 2012 十二月 7

All Science Journal Classification (ASJC) codes

  • 化學 (全部)
  • 材料化學

指紋

深入研究「Bipolar material with spiro-fluorenyl terminals: Synthesis, characterization and application for enhancement of electrophosphorescence」主題。共同形成了獨特的指紋。

引用此