Bone formation at the surface of low modulus Ti-7.5Mo implants in rabbit femur

Dan Jae Lin, Cheng Chung Chuang, Jiin Huey Chern Lin, Jing Wei Lee, Chien Ping Ju, Hsiang Shu Yin

研究成果: Article同行評審

100 引文 斯高帕斯(Scopus)

摘要

The biocompatibility of the Ti-7.5Mo alloy was examined, because the alloy has a high-strength/modulus ratio and thus is a potential candidate for orthopedic applications. Cell viability assay using 3T3 cells revealed that the Ti-7.5Mo did not induce apparent cell death, when the cells were grown on disks made of the alloy or incubated with the alloy-conditioned medium at 37 or 72 °C for 24-72 h. The Ti-6Al-4V alloy was used as a control and did not cause apparent cell death either. Moreover, pins of 6 mm long and 2 mm in diameter of Ti-7.5Mo and Ti-6Al-4V were implanted into the left and right rabbit femurs, respectively, for 6, 12 and 26 weeks. New bone tissue grew to surround the pins, which spanned cortical and marrow regions, as shown by toluidine blue-stained bone sections of the three time points. Strikingly, the amount of new bone encircling the Ti-7.5Mo implant was approximate two-folds of that at Ti-6Al-4V by 26 weeks post-implantation. This facilitation of bone formation could be associated with the unique properties, such as a low modulus and the composition of Mo, of the Ti-7.5Mo.

原文English
頁(從 - 到)2582-2589
頁數8
期刊Biomaterials
28
發行號16
DOIs
出版狀態Published - 2007 6月

All Science Journal Classification (ASJC) codes

  • 生物物理學
  • 生物工程
  • 陶瓷和複合材料
  • 生物材料
  • 材料力學

指紋

深入研究「Bone formation at the surface of low modulus Ti-7.5Mo implants in rabbit femur」主題。共同形成了獨特的指紋。

引用此