Carbon black sintering effects on the composition of multiphase calcium phosphate bioceramics

Wen Cheng Chen, Chien Ping Ju, Wen Hsien Cheng, Jiin Huey Chern Lin

研究成果: Article同行評審

5 引文 斯高帕斯(Scopus)

摘要

The presence of carbonate (CO32-) combined with calcium phosphates has been believed to increase the susceptibility of natural bone formation. This study was carried out to investigate the thermal properties of apatite in nano scale precipitates with added carbon black that could act as a sintering inhibitor and a carbonate preserver. In addition, the present study aimed to determine the effects of those additives and analyze their chemical compositions. Ceramics processed at different heating temperatures were compared and characterized. The results showed that a multiphase ceramic of apatite-calcium carbonate (CaCO3)-calcium oxide (CaO) was formed in a temperature range of 600 to 800 °C. By observing the morphologies of the ceramics, the addition of carbon black which acts as a carbonate supplier in the heating processes and further as an inhibitor to prevent the sintering effect of the nano scale particles in sub-micro range efficiently at 1400 °C were established.

原文English
頁(從 - 到)279-283
頁數5
期刊Journal of Ceramic Processing Research
14
發行號3
出版狀態Published - 2013 十一月 6

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites

指紋 深入研究「Carbon black sintering effects on the composition of multiphase calcium phosphate bioceramics」主題。共同形成了獨特的指紋。

引用此