Characteristics and cyto-compatibility of Collagen/Ca-P coatings on Ti6Al4V substrate

Rex C.C. Wang, Ming Che Hsieh, Shih Ping Yang, Po Kai Chuang, Jui Che Lin, Chyun Yu Yang, Tzer Min Lee

研究成果: Article同行評審

15 引文 斯高帕斯(Scopus)

摘要

The surface modification method for a substrate affects its cyto-compatibility. Collagen coating has been considered as an effective way to vary the biological interactions occurring on the Ti6Al4V substrate. However, a uniform collagen coating is difficult to be prepared by direct collagen coating method. In this study, a simple and efficient method was developed to coat a homogenous collagen top layer on a Ti6Al4V sample that was precoated with a biomimetic Ca-P intermediate layer. Scanning electron microscopy (SEM) observations show that a non-uniform collagen coating formed on the surface of a pristine Ti6Al4V substrate, whereas a continuous and homogenous collagen coating formed on a Ti6Al4V surface pre-coated with Ca-P. Human osteosarcoma cells (HOS) were cultured and their cell morphology examined using SEM after 3 and 24. h. After seeding the cultured cell onto the substrates, cell proliferation was measured using the AlamarBlue assay at 1, 5, and 10. days. It was found that cells seeded onto collagen and Collagen/Ca-P coated substrates yielded well-developed filopodia and lamellipodia. However, the cell proliferation of Collagen/Ca-P was significantly higher than those of the other specimen for 5- and 10-day culture specimen. These results suggest that the proposed method can be used to deposit a uniform collagen coating on specimens for biomedical applications.

原文English
頁(從 - 到)4683-4689
頁數7
期刊Surface and Coatings Technology
205
發行號19
DOIs
出版狀態Published - 2011 6月 25

All Science Journal Classification (ASJC) codes

  • 一般化學
  • 凝聚態物理學
  • 表面和介面
  • 表面、塗料和薄膜
  • 材料化學

指紋

深入研究「Characteristics and cyto-compatibility of Collagen/Ca-P coatings on Ti6Al4V substrate」主題。共同形成了獨特的指紋。

引用此