Characteristics of ZnCdTe grown on (100) GaAs substrate by MOCVD

P. W. Sze, N. F. Wang, M. P. Houng, Y. H. Wang, Y. T. Cherng, C. H. Wang

研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)

摘要

To predict the Zn composition accurately in the ZnCdTe compound alloys, the estimation of solid-vapor distribution functions (SVDFs) from equilibrium thermodynamics on ternary II-VI compound semiconductors is applied to the growth of ZnCdTe alloys. Epitaxial layers of ZnCdTe grown on (100) GaAs substrates were performed by metalorganic chemical vapor deposition using DMCd, DETe, and DEZn as the material sources. Surface morphologies, film orientations, optical properties and quality of ZnCdTe epilayers related to the growth conditions were characterized by optical microscopy, X-ray diffraction, photoluminescence, and X-ray double-crystal rocking curve (DCRC) measurements. The best film quality was reported at a growth temperature of 350°C with a VI/II ratio of 0.57. The corresponding full width at half-maximum (FWHM) and x values of ZnxCd1-xTe films measured by DCRC and scanning electron microscope energy dispersive X-ray analysis were 180 arcsec and 0.07, respectively. The measured Zn composition in ZnCdTe can be estimated from the calculated results with good agreement.

原文English
頁(從 - 到)27-32
頁數6
期刊Journal of Crystal Growth
169
發行號1
DOIs
出版狀態Published - 1996 十一月

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Inorganic Chemistry
  • Materials Chemistry

指紋 深入研究「Characteristics of ZnCdTe grown on (100) GaAs substrate by MOCVD」主題。共同形成了獨特的指紋。

引用此