Complex susceptibilities of Co-substituted YBa2Cu3O7-d synthesized by the polymerized complex method

Hiromasa Mazaki, Hiroshi Yasuoka, Masato Kakihana, Hirotaka Fujimori, Masatomo Yashima, Masahiro Yoshimura

研究成果: Article同行評審

12 引文 斯高帕斯(Scopus)

摘要

Practically impurity-free ceramic samples of YBa2Cu3-xCoxO7-d with x = 0-0.5 and Y0.8Ca0.2Ba2Cu2.8Co0.2O7-d were synthesized by the polymerized complex method through two different routes, starting either from metal nitrates (route P) or from metal carbonates (route Q). Better compositional homogeneity was achieved in the latter route, where neither colloids nor precipitates were formed during the polymerization procedure. The magnetic response of the samples was measured in terms of AC magnetic susceptibilities and variation of the onset temperature Tc(onset) of the superconducting transition was precisely determined as a function of Co content. The Tc(onset) were almost unaffected for 0 ≤ x ≤ 0.5, decreased linearly with ΔTc/Δx ∼ -220 K for 0.07 ≤ x ≤ 0.3, and the superconductivity vanished for x ≥ 0.4. The depression of Tc was interpreted in terms of the localization of holes in the Cu(1)Oy planes. The replacement of 20% of Y with Ca in YBa2Cu2.8Co0.2O7-d enhanced Tc from the initial value of 57.1 K up to 88.6 K. It was suggested that the rise in Tc induced by Ca doping was connected with the delocalization effect of holes in which the hole charge transfer from the Cu(1)Oy planes to the Cu(2)O2 conduction sheets played a crucial role.

原文English
頁(從 - 到)37-45
頁數9
期刊Physica C: Superconductivity and its applications
246
發行號1-2
DOIs
出版狀態Published - 1995 五月 1

All Science Journal Classification (ASJC) codes

  • 電子、光磁材料
  • 凝聚態物理學
  • 能源工程與電力技術
  • 電氣與電子工程

指紋

深入研究「Complex susceptibilities of Co-substituted YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-d</sub> synthesized by the polymerized complex method」主題。共同形成了獨特的指紋。

引用此