Consideration of kinetics on intermetallics formation in solid-solution high entropy alloys

T. H. Chou, J. C. Huang, C. H. Yang, S. K. Lin, T. G. Nieh

研究成果: Article

1 引文 斯高帕斯(Scopus)

摘要

There are overwhelming experimental observations indicating intermetallic (IM) phase formed in the intermediate temperatures in high entropy alloys. In this study, we proposed a model to show how kinetics could intervene the thermodynamic determination of phase formation. The model offers a good explanation for the prevalent formation of IM formation in the intermediate temperature range in high entropy alloys available in the literature. To further demonstrate the kinetic effect, we selected the equiatomic CrMnFeCoNi alloy (i.e., Cantor Alloy) as a surrogate material and employed differential scanning calorimetry (DSC) at different heating rates to investigate IM formation in this alloy. In this case, we found the presence of four IM compounds, BCC-Cr, L10-NiMn, B2-FeCo, and Cr-rich σ phases, in the temperature ranging from about 200 to 900°C, above which the alloy was a complete solid solution. From the DSC measurements, we were also able to build a quasi-equilibrium TTT diagram for Cantor Alloy. It was the first time that such a TTT diagram was established for a high entropy alloy.

原文English
頁(從 - 到)71-80
頁數10
期刊Acta Materialia
195
DOIs
出版狀態Published - 2020 八月 15

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Polymers and Plastics
  • Metals and Alloys

指紋 深入研究「Consideration of kinetics on intermetallics formation in solid-solution high entropy alloys」主題。共同形成了獨特的指紋。

  • 引用此