The SBA-1 mesoporous silica of Pm3̄n symmetry with different pore sizes have been conveniently prepared from a dilute aqueous solution of C nTMAX (n = 14-18, X = Br, Cl) and sodium silicate at pH value of 2.0. A mesophase transformation from cubic Pm3̄n to hexagonal p6mm occurs at relatively high surfactant concentration of about 6.0 × 10-2 M. Moreover, a slow self-assembling reaction in a dilute solution leads to the formation of the mesostructural SBA-1 crystals. The SBA-1 crystal shape also changes with the chain length of the surfactant. Basically, crystallization processes are thermodynamically and kinetically controlled. Many synthetic factors (such as pH value, silica/surfactant ratio, concentration of the surfactant and temperature) which can influence the silica condensation rate, surfactant micellization and surface free energy of the crystal have apparent effects on the crystal morphology of the SBA-1 mesoporous silica. The organic silica source (tetraethyl orthosilicate, TEOS) can serve as an alternative silica source to obtain the SBA-1 mesoporous silica crystals, but a longer aging time is needed than that of acidified sodium silicate.

原文English
頁(從 - 到)269-276
頁數8
期刊Microporous and Mesoporous Materials
83
發行號1-3
DOIs
出版狀態Published - 2005 9月 1

All Science Journal Classification (ASJC) codes

  • 化學 (全部)
  • 材料科學(全部)
  • 凝聚態物理學
  • 材料力學

指紋

深入研究「Controlling the crystal morphology of mesoporous silica SBA-1」主題。共同形成了獨特的指紋。

引用此