Corrosion of stainless steel coated with TiN, (TiAl)N and CrN in aqueous environments

M. A.M. Ibrahim, S. F. Korablov, M. Yoshimura

研究成果: Article同行評審

82 引文 斯高帕斯(Scopus)

摘要

The corrosion behaviour of TiN, (TiAl)N and CrN coated on 304 stainless steel by physical vapour deposition was examined in borate solution (pH 9.0) and in 0.5 M NaCl solution. The study was performed by using open circuit potential, potentiodynamic polarization and cyclic polarization techniques, complemented with XRD and laser microscopy. The measurements were also performed on the uncoated substrate for comparison. Nitrided coatings significantly improve the corrosion performance of the steel; however, they are prone to corrosive attack as a consequence of the presence of microstructure defects such as pinholes and pores. Galvanic corrosion between the coatings and the substrate result in significant attack of the substrate, allowed by the penetration of small pinholes into the substrate. In borate solution, (TiAl)N possesses the highest corrosion resistance. However, CrN possessed the highest corrosion resistance in NaCl solution.

原文English
頁(從 - 到)815-828
頁數14
期刊Corrosion Science
44
發行號4
DOIs
出版狀態Published - 2002 四月

All Science Journal Classification (ASJC) codes

  • 化學 (全部)
  • 化學工程 (全部)
  • 材料科學(全部)

指紋

深入研究「Corrosion of stainless steel coated with TiN, (TiAl)N and CrN in aqueous environments」主題。共同形成了獨特的指紋。

引用此