Corrosion resistance of aluminum nitride as semiconductor equipment parts studied by micro-Raman spectroscopy

Hirotaka Fujimori, Yoji Tamura, Akira Harita, Koji Ioku, Masato Kakihana, Masahiro Yoshimura, Seishi Goto

研究成果: Article同行評審

3 引文 斯高帕斯(Scopus)

摘要

A micro-Raman spectroscopic investigation has been performed to observe structural disorder in each grain of aluminum nitride ceramics as semiconductor equipment parts. A selective thermal oxidation treatment normalizes a different rate of a corrosion reaction depending on the crystal face and consequently improves the corrosion resistance. Upon thermal oxidation treatment, line widths of Raman bands increased more in grains including mainly crystals with (100) preferred orientation than in those of (002), indicating that (100) faces oxidize preferentially rather than (002) faces. According to Raman shift from the oxidized sample, oxidation induces residual compressive stress for grains including a large number of (100) prefer-oriented crystals. On fluorination of the oxidized sample, no increase of line widths was observed in both kinds of grains, suggesting that prior anisotropic thermal oxidation treatment of (100) faces, which are more sensitive to corrosion than (002) faces, inhibits the progress of corrosion.

原文English
頁(從 - 到)935-938
頁數4
期刊Journal of the Ceramic Society of Japan
111
發行號1300
DOIs
出版狀態Published - 2003 十二月

All Science Journal Classification (ASJC) codes

  • 陶瓷和複合材料
  • 化學 (全部)
  • 凝聚態物理學
  • 材料化學

指紋

深入研究「Corrosion resistance of aluminum nitride as semiconductor equipment parts studied by micro-Raman spectroscopy」主題。共同形成了獨特的指紋。

引用此