Crystal Structure and ferroelectric properties of (Bi0.5Na 0.5)TiO3-Ba(Zr0.05Ti0.95)O 3 piezoelectric ceramics

Wei Chih Lee, Yi Fang Lee, Min Hui Tseng, Chi Yuen Huang, Yu Chun Wu

研究成果: Article同行評審

22 引文 斯高帕斯(Scopus)

摘要

The crystal structure and ferroelectric properties of (1-x)(Bi 0.5Na0.5)TiO3-xBa(Zr0.05Ti 0.95)O3 (BNBZTx, x≤12%) lead-free piezoelectric ceramics were studied. The distance between the centers of cations and anions (dc-a) as well as the lattice parameters was carefully investigated by Rietveld refinement on X-ray diffraction patterns. It was found that the crystal phase was determined by the amount of Ba(Zr0.05Ti 0.95)O3 added, whereas the pure rhombohedral and tetragonal phases are observed in compositions containing x≤4 and x≥8%, respectively. A rhombohedral-tetragonal morphotropic phase boundary (MPB) was found at around BNBZT6, which showed a maximum and minimum dc-a at its rhombohedral and tetragonal phases, respectively. According to the present study, the ferroelectric properties show a strong dependence on their crystal phases. For the single-phase compositions, the remanent polarization (P r) generally increased with the value of dc-a while their coercive fields (Ec) were determined by their lattice parameters. Nevertheless, the behavior in Pr and Ec for MPB compositions is related to not only the lattice parameter but also the composed phases.

原文English
頁(從 - 到)1069-1073
頁數5
期刊Journal of the American Ceramic Society
92
發行號5
DOIs
出版狀態Published - 2009 5月

All Science Journal Classification (ASJC) codes

  • 陶瓷和複合材料
  • 材料化學

指紋

深入研究「Crystal Structure and ferroelectric properties of (Bi0.5Na 0.5)TiO3-Ba(Zr0.05Ti0.95)O 3 piezoelectric ceramics」主題。共同形成了獨特的指紋。

引用此