Crystallization behavior and microstructure of silica-free 5K 2O-45CaO-50P2O5 bioglass

Moo Chin Wang, You Cheng Lai, Wei Jen Shih, Ping Yu Shih, Guo Ju Chen, Wang Long Li

研究成果: Article同行評審

1 引文 斯高帕斯(Scopus)

摘要

The crystallization behavior and microstructure of silica-free 5K 2O-45CaO-50P2O5 (KCP) bioglass have been studied using differential thermal analysis (DTA), X-ray diffraction (XRD), scanning election microscopy (SEM), transmission electron microscopy (TEM), and selected area electron diffraction (SAED). The activation energy for the KCP bioglass crystallization is found to be 337.4 kJ/mol using a nonisothermal method. The crystalline phases of the glass surface determined by XRD are KCa(PO3)3, 4CaO•3P2O5, and β-Ca(PO3)2 when the KCP bioglass is crystallized at 903 K for 4 hours. The crystalline phase of the powder samples determined by XRD is β-Ca(PO3)2 when silica-free KCP glasses crystallized at 873 to 1073 K for 8 hours. Crystallization starts at the surface of the KCP bioglass and then proceeds toward the interior of the glass matrix. The morphology of β-Ca(PO3)2 is a fibrillar shape 20 to 180 nm in length and 17 to 20 nm in diameter, with an aspect ratio ranging from 1.0 to 10.6.

原文English
頁(從 - 到)297-307
頁數11
期刊Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
41
發行號2
DOIs
出版狀態Published - 2010 二月

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys

指紋 深入研究「Crystallization behavior and microstructure of silica-free 5K <sub>2</sub>O-45CaO-50P<sub>2</sub>O<sub>5</sub> bioglass」主題。共同形成了獨特的指紋。

引用此