CRYSTALLIZATION OF MULLITE-ZIRCONIA AMORPHOUS MATERIALS PREPARED BY RAPID-QUENCHING.

Masahiro Yoshimura, Masafumi Kaneko, Shigeyuki Somiya

研究成果: Article同行評審

6 引文 斯高帕斯(Scopus)

摘要

Amorphous materials have been prepared by rapid quenching, approximately 10**5** degree C/s, of the melt of the mixed oxides, 20wt% ZrO//2-80wt% (3. 4 Al//2O//3 multiplied by (times) 2 SiO//2) using an arc-imaging furnace and a twin-roller. This paper deals with the crystallization and the products of these amorphous materials obtained by reheating under various conditions. The crystallization of this amorphous material took place at approximately 990 degree C precipitating t-ZrO//2 and mullite phases after showing glass-transition temperature at 919 degree C on heating by 10 degree C/min. The mullite had markedly larger lattice parameters than that of stoichiometric mullite (3Al//2O//3 multiplied by (times) 2SiO//2) indicating higher ( greater than 83wt%) Al//2O//3 contents in the early stage of crystallization, then showed smaller lattice parameters on prolonged reheating.

原文English
頁(從 - 到)202-208
頁數7
期刊Yogyo Kyokai Shi/Journal of the Ceramic Society of Japan
95
發行號2 pt 2
出版狀態Published - 1987

All Science Journal Classification (ASJC) codes

  • 工程 (全部)

指紋

深入研究「CRYSTALLIZATION OF MULLITE-ZIRCONIA AMORPHOUS MATERIALS PREPARED BY RAPID-QUENCHING.」主題。共同形成了獨特的指紋。

引用此