CVD growth of large-area InS atomic layers and device applications

Chien Liang Tu, Kuang I. Lin, Jiang Pu, Tsai Fu Chung, Chien Nan Hsiao, An Ci Huang, Jer Ren Yang, Taishi Takenobu, Chang Hsiao Chen

研究成果: Article

摘要

Group-III monochalcogenides of two-dimensional (2D) layered materials have attracted widespread attention among scientists due to their unique electronic performance and interesting chemical and physical properties. Indium sulfide (InS) is attracting increasing interest from scientists because it has two distinct crystal structures. However, studies on the synthesis of highly crystalline, large-area, and atomically thin-film InS have not been reported thus far. Here, the chemical vapor deposition (CVD) synthesis method of atomic InS crystals has been reported in this paper. The direct chemical vapour phase reaction of metal oxides with chalcogen precursors produces a large-sized hexagonal crystal structure and atomic-thickness InS flakes or films. The InS atomic films are merged with a plurality of triangular InS crystals that are uniform and entire and have surface areas of 1 cm2 and controllable thicknesses in bilayers or trilayers. The properties of the as-grown highly crystalline samples were characterized by spectroscopic and microscopic measurements. The ion-gel gated InS field-effect transistors (FETs) reveal n-type transport behavior, and have an on-off current ratio of >103 and a room-temperature electron mobility of ∼2 cm2 V-1 s-1. Moreover, our CVD InS can be transferred from mica to any substrates, so various 2D materials can be reassembled into vertically stacked heterostructures, thus facilitating the development of heterojunctions and exploration of the properties and applications of their interactions.

原文English
頁(從 - 到)9366-9374
頁數9
期刊Nanoscale
12
發行號17
DOIs
出版狀態Published - 2020 五月 7

All Science Journal Classification (ASJC) codes

  • Materials Science(all)

指紋 深入研究「CVD growth of large-area InS atomic layers and device applications」主題。共同形成了獨特的指紋。

  • 引用此

    Tu, C. L., Lin, K. I., Pu, J., Chung, T. F., Hsiao, C. N., Huang, A. C., Yang, J. R., Takenobu, T., & Chen, C. H. (2020). CVD growth of large-area InS atomic layers and device applications. Nanoscale, 12(17), 9366-9374. https://doi.org/10.1039/d0nr01104e