Dependence of damage and strain on the temperature of Si irradiation in epitaxial Ge0.10Si0.90 films on Si(100)

D. Y.C. Lie, J. H. Song, A. Vantomme, F. Eisen, M. A. Nicolet, N. D. Theodore, T. K. Carns, K. L. Wang

研究成果: Article同行評審

8 引文 斯高帕斯(Scopus)


Damage and strain produced in a 370-nm-thick strained epitaxial Ge 0.10Si0.90 film on Si(100) by irradiation with 320 keV 28Si+ ions at fixed temperatures ranging from 40 to 150°C and for doses from 1 to 30×1014/cm2 have been measured by MeV 4He channeling spectrometry, transmission electron microscopy, and high-resolution x-ray diffractometry. The ion energy was chosen so that the maximum damage created by irradiation occurs very near the GeSi-Si interface. For all temperatures, the retained damage and the perpendicular strain induced by the irradiation are significantly greater in the GeSi epilayer than in the Si substrate. For all doses the retained damage and the induced perpendicular strain become small above 100°C. Both rise nonlinearly with increasing ion dose. They are related to each other differently in GeSi than in bulk Si or Ge irradiated at room temperature. Postirradiation furnace annealing can remove a large portion of the induced damage and strain for nonamorphized samples. Amorphized samples regrow by solid-phase epitaxy after annealing at 550°C for 30 min; the regrown GeSi is, however, highly defective and elastically relaxed. A consequence of this defectiveness is that irradiation-induced amorphization in metastable GeSi is undesirable for applications where good crystalline quality is required. Ion implantation above room temperature can prevent amorphization.

頁(從 - 到)2329-2338
期刊Journal of Applied Physics
出版狀態Published - 1995

All Science Journal Classification (ASJC) codes

  • 物理與天文學 (全部)


深入研究「Dependence of damage and strain on the temperature of Si irradiation in epitaxial Ge0.10Si0.90 films on Si(100)」主題。共同形成了獨特的指紋。