Designing Co3O4/silica catalysts and intensified ultrafiltration membrane-catalysis process for wastewater treatment

Jia Ding, Gholamreza Vahedi Sarrigani, Jiangtao Qu, Amirali Ebrahimi, Xia Zhong, Wen Che Hou, Julie M. Cairney, Jun Huang, Dianne E. Wiley, David K. Wang

研究成果: Article同行評審

摘要

An integrated cobalt oxide catalyst supported on silica (Co3O4/SiO2) packed in the lumen of tubular alumina (Al2O3) membrane was designed to realize a Fenton-like oxidation coupling with ultrafiltration water treatment technology to remove persistent and hazardous pollutants. We employed a selection of SiO2 support materials with a range micro/mesostructures to immobilize the Co3O4 catalyst. These were evaluated and screened to achieve the highest pollutant decolorization rate and maximum decolorization efficiency. Then, an integrated catalyst-membrane was developed as proof-of-concept for advanced water treatment. Batch degradation results showed acid orange 7 dye (AO7) was effectively removed using Co3O4 deposited on MCM-41 silica, with 97% decolorization efficiency achieved in 15 mins owing to the large surface area and high porosity of the MCM-41 support. In contrast, humic acid (HA) was relatively difficult to degrade using this catalyst, and was however found to inhibit AO7 degradation. The integrated catalyst-membrane successfully removed both AO7 and HA with only a 10% water flux reduction from 25.0 to 22.5 kg m−2 h−1 bar−1 with excellent co-pollutant removal rate of 99% over 40 h. Furthermore, the integrated catalyst-membrane also removed a range of organic pollutants (neutral red, tetracycline hydrochloride, oxytetracycline) achieving > 90% rejection and 30 kg m−2 h−1 bar−1. These results show that the integrated catalyst-membrane can effectively purify a binary pollutant mixture containing both hazardous dye and natural organic matter and other pharmaceutical chemicals whilst producing process water for recycling and reuse.

原文English
文章編號129465
期刊Chemical Engineering Journal
419
DOIs
出版狀態Published - 2021 九月 1

All Science Journal Classification (ASJC) codes

  • 化學 (全部)
  • 環境化學
  • 化學工程 (全部)
  • 工業與製造工程

指紋

深入研究「Designing Co<sub>3</sub>O<sub>4</sub>/silica catalysts and intensified ultrafiltration membrane-catalysis process for wastewater treatment」主題。共同形成了獨特的指紋。

引用此