Determination of activation behavior in annealed Al-N codoped ZnO films

Shiau Lu Yao, Jhen Dong Hong, Ching Ting Lee, Chung Yen Ho, Day Shan Liu

研究成果: Article同行評審

25 引文 斯高帕斯(Scopus)

摘要

Al-N codoped ZnO films prepared via cosputtering technology were postannealed at 450 C for 30 min under ambient vacuum and nitrogen. The extrinsic impurities in these annealed samples, resulting in evolutions on the carriers and radiation emissions, were investigated through their photoluminescence spectra and Hall-effect measurements. It was found that the donor-acceptor-pair emission was related to the VZn-AlZn transition at 2.86 eV and predominated over the defect-transition luminescence in the room-temperature photoluminescence (RTPL) spectrum of the vacuum-annealed sample, which possessed a high electron carrier concentration. With the help of temperature-dependent Hall measurements, a shallow donor level corresponding to Al on the Zn site (AlZn) was derived as EC - (51 4) meV. In contrast, the defect-transition luminescence in the RTPL spectrum of the nitrogen-annealed Al-N codoped ZnO film, showing p-type conduction with a hole concentration of 1018 cm-3, was dominated by the V O-NO deep level emission at approximately 1.87 eV. The estimated acceptor level corresponding to the N on the O site (NO) was EV (149 6) meV. The binding energy and the activation energy associated with the NO acceptor were also determined by the low-temperature photoluminescence and temperature-dependent PL spectra.

原文English
文章編號103504
期刊Journal of Applied Physics
109
發行號10
DOIs
出版狀態Published - 2011 5月 15

All Science Journal Classification (ASJC) codes

  • 物理與天文學 (全部)

指紋

深入研究「Determination of activation behavior in annealed Al-N codoped ZnO films」主題。共同形成了獨特的指紋。

引用此