Dielectric properties and microstructure of Nb-Co codoped BaTiO 3-(Bi0.5Na0.5)TiO3 ceramics

Hsing I. Hsiang, Li Then Mei, Yi Jih Chun

研究成果: Article

20 引文 斯高帕斯(Scopus)

摘要

X-ray diffractometry, scanning electron microscopy, transmission electron microscopy, and an impedance analyzer were used to examine the Nb-Co codoping effects on the densification, crystalline phase, microstructure development, and dielectric-temperature characteristics of BaTiO3-(Bi 0.5Na0.5)TiO3 ceramics. The results indicate that the Curie temperature shifted to a higher temperature (above 140°C) by adding BNT. The dielectric constant-temperature (ε-T) curve broadened at the Curie temperature due to the small grain size (0.3-0.4 μm). A core-shell structure was developed, which is helpful to flatten the ε-T curve of BaTiO3 ceramics at high temperatures.

原文English
頁(從 - 到)2768-2771
頁數4
期刊Journal of the American Ceramic Society
92
發行號11
DOIs
出版狀態Published - 2009 十一月 1

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Materials Chemistry

指紋 深入研究「Dielectric properties and microstructure of Nb-Co codoped BaTiO <sub>3</sub>-(Bi<sub>0.5</sub>Na<sub>0.5</sub>)TiO<sub>3</sub> ceramics」主題。共同形成了獨特的指紋。

  • 引用此