Dielectric properties and mixture behavior of Mg4Nb2O9-SrTiO3 ceramic system at microwave frequency

Cheng-Liang Huang, Jhih Yong Chen, Chih Chao Liang

研究成果: Article

16 引文 斯高帕斯(Scopus)

摘要

The microwave dielectric properties and the microstructures of the (1 - x)Mg4Nb2O9-xSrTiO3 ceramic system prepared by the conventional solid-state route were investigated. SrTiO3 was employed as a τf compensator and was added to Mg4Nb2O9 to achieve a temperature-stable material. Corundum-structured Mg4Nb2O9 and perovskite-structured SrTiO3 were coexisted and the two-phase system was confirmed by the XRD and EDX analysis. Dielectric properties are correlated to the sintering temperature and the compositional ratio of the specimens. Although the εr of the specimen could be boosted by increasing amount of SrTiO3, it would instead render a decrease in the Q × f. The τf value is strongly correlated to the compositions and can be controlled through the existing phases. In fact, τf could be adjusted to near-zero by mixing 60 mole% Mg4Nb2O9 and 40 mole% SrTiO3. A dielectric constant (εr) of 21.02, a high Q × f value of 112,000 GHz (measured at 9.7 GHz) and a temperature coefficient of resonant frequency (τf) of 1.6 ppm/°C were obtained for 0.6Mg4Nb2O9-0.4SrTiO3 sintered at 1300 °C for 4 h. It is proposed as a very promising dielectric material for low-loss microwave and millimeter wave applications.

原文English
頁(從 - 到)554-558
頁數5
期刊Journal of Alloys and Compounds
478
發行號1-2
DOIs
出版狀態Published - 2009 六月 10

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

指紋 深入研究「Dielectric properties and mixture behavior of Mg<sub>4</sub>Nb<sub>2</sub>O<sub>9</sub>-SrTiO<sub>3</sub> ceramic system at microwave frequency」主題。共同形成了獨特的指紋。

  • 引用此