Dielectric properties of (1-y)Ca1-xLa2x/3TiO3-y(Li,Nd)1/2 TiO3 ceramic system at microwave frequency

Cheng Liang Huang, Jsung Ta Tsai, Yuan Bin Chen

研究成果: Article同行評審

82 引文 斯高帕斯(Scopus)

摘要

The solid solution of dielectric ceramic Ca1-xLa2x/3TiO3 system for the composition range of 0.1 ≤ x ≤ 0.9 is studied. The crystal structure of the system is single perovskite. From the X-ray diffraction patterns, the superstructure reflection lines are detected for the composition x ≥ 0.5. With an increase in the substitution amount of La, the permittivity and the temperature coefficient of resonant frequency (TCF) decrease. A maximum Q × f value of 17600 appears at x = 0.4 since that the extrinsic origin for the dielectric loss degrades the Q × f value due to the poor grain growth for the composition x ≥ 0.5. (1-y)Ca1-xLa2x/3TiO3-y(Li,Nd)1/2 TiO3 compounds are introduced to obtain a good temperature stability of resonant frequency. With x = 0.4, the composition y = 0.5 shows good temperature stability (τf = +4.5ppm/°C) with a high permittivity of 105 and a Q × f value of 7000 GHz.

原文English
頁(從 - 到)547-556
頁數10
期刊Materials Research Bulletin
36
發行號3-4
DOIs
出版狀態Published - 2001 2月

All Science Journal Classification (ASJC) codes

  • 一般材料科學
  • 凝聚態物理學
  • 材料力學
  • 機械工業

指紋

深入研究「Dielectric properties of (1-y)Ca1-xLa2x/3TiO3-y(Li,Nd)1/2 TiO3 ceramic system at microwave frequency」主題。共同形成了獨特的指紋。

引用此