Direct fabrication of CaWO4 patterns on cellulose based organic substrates by on-site ink-jet reaction at room temperature

Ruwan Gallage, Ryo Teranishi, Takeshi Fujiwara, Tomoaki Watanabe, Masahiro Yoshimura

研究成果: Article同行評審

6 引文 斯高帕斯(Scopus)

摘要

We have employed ink-jet reaction method for direct fabrication of calcium tungstate patterns with the minimum width of around 150 μm on cellulose based organic substrates without any post-firing and/or sintering. The XRD patterns revealed that the formed phase was a well-crystallized single phase of CaWO4 without any other impurity phases and the crystallite size was about 20 ± 4 nm. The Raman spectra were further confirmed the fabricated patterns consisted of CaWO4. The adhesion of CaWO4 to the substrate was good and revealed by SEM observations. The patterned CaWO4 showed the original blue luminescence when exposed to ultraviolet radiation (wavelength 254 nm) under dark room conditions at room temperature.

原文English
頁(從 - 到)299-303
頁數5
期刊Materials Science and Engineering B: Solid-State Materials for Advanced Technology
137
發行號1-3
DOIs
出版狀態Published - 2007 2月 25

All Science Journal Classification (ASJC) codes

  • 材料科學(全部)
  • 凝聚態物理學
  • 材料力學
  • 機械工業

指紋

深入研究「Direct fabrication of CaWO4 patterns on cellulose based organic substrates by on-site ink-jet reaction at room temperature」主題。共同形成了獨特的指紋。

引用此