Doping effects of CuO additives on the properties of low-temperature- sintered PMnN-PZT-based piezoelectric ceramics and their applications on surface acoustic wave devices

Cheng Che Tsai, Sheng Yuan Chu, Chun Hsien Lu

研究成果: Article

10 引文 斯高帕斯(Scopus)

摘要

To develop the anisotropic ceramic substrate with low sintering temperature for surface acoustic wave (SAW) applications, the low cost and feasible material with moderate piezoelectric properties, good dielectric properties, and higher Curie temperature were explored. The piezoelectric ceramics with compositions of Pb[(Mn1/3Nb2/3/)/sub 0.06-/(Zr0.52 Ti0.48)0.94] O 3 (PMnN-PZT) + 0.5 wt.% PbO + x wt.% CuO (0.05≤ x≤ 0.3) had been prepared by the conventional mixed-oxides method. CuO dopants were used as the sintering aid to improve the bulk density under low sintering temperature (i.e., 980-1040°C). The phase structures, microstructures, frequency behavior of dielectric properties (up to 50 MHz), piezoelectric properties, ferroelectric properties, and temperature stability with the amount of CuO additive were systematically investigated. Experimental results showed that the sintering temperature could be lowered down to 1020°C and still keep reasonably good piezoelectric activity (i.e., high electromechanical coupling factor kp , kt) and dielectric and ferroelectric properties. The preferable composition, obtained at x = 0.1, presented the values of the electromechanical coupling factor (kp) (kt), mechanical quality factor (Qm/), piezoelectric charge constant (d33), dielectric constant, dielectric loss, temperature coefficient of resonant frequency (TCFB), and Curie point (Tc) of 0.54, 0.48, 850, 238 pc/N, 1450, 0.0023, 1.1 kV/mm, 26 coul/cm/sup 2/,-150 ppm/°C, and 348°C. Using this developed low-temperature-sintered material to make the piezoelectric substrate, the SAW filter was fabricated and its properties were measured. Results showed that this device possessed very high value of k2(7.13%) with a good TCF (40.15 ppm/°C), and a surface wave velocity (V/sub P/) of 2196 m/s.

原文English
文章編號4816073
頁(從 - 到)660-668
頁數9
期刊IEEE Transactions on Ultrasonics, Ferroelectrics, and Frequency Control
56
發行號3
DOIs
出版狀態Published - 2009 三月 1

All Science Journal Classification (ASJC) codes

  • Instrumentation
  • Acoustics and Ultrasonics
  • Electrical and Electronic Engineering

指紋 深入研究「Doping effects of CuO additives on the properties of low-temperature- sintered PMnN-PZT-based piezoelectric ceramics and their applications on surface acoustic wave devices」主題。共同形成了獨特的指紋。

  • 引用此